Resisting Failure if Treated with Care


A pavement is about 93-96% rock, by weight, however it seems that there is a strong belief that by properly modifying the asphalt all problems can be solved. Asphalt or more properly, asphalts have served us well, even before modification. The properties of asphalts are primarily determined by their crude sources, however blending crudes or asphalts can at times produce an asphalt that performs better than either of the components. Modifying asphalts can also enhance their properties. However, it is important that we keep in mind that its performance depends to a great extent to its ability to flow, and its ability to suppress hardening as time goes.

Rutting is Not an Asphalt Failure. Asphalt is a liquid whose job is to flow in response to stress. If a pavement ruts, it is either ground by studded tires, or the aggregate size or the gradation is improper. If the stress is greater than the aggregate can handle, rutting occurs with the asphalt doing what it is designed to do, flow. Modifying the asphalt can affect how fast the flow occurs, however it is the aggregate properties that affect the rutting.

Many Aggregates Prefer Water to Asphalt. Asphalt doesn’t work well if it can’t stick to aggregate. Water can interfere with adhesion. One cause can be in the asphalt itself. If it is produced from crude oil that had been treated with caustic soda, it will contain soaps that will make the asphalt itself water sensitive. That has been solved by lime treating the crude. Antistrips are used to aid adhesion; however it has been shown that with some antistrips the effect wears off which allows water to lift the asphalt off of the rocks. There is one antistrip that combines chemically to aggregate and provides long term durability.

Non-load Associated Cracking Occurs when the Asphalt Cannot Relax Stresses. The fluidity of the asphalt is essential to prevent cracking. Trying to make the asphalt stronger only makes the matter worse as its maximum tensile strength is about 1000 psi. Portland cement cannot defeat thermal stress so don’t expect asphalt to do so. The solution is to have a binder that can relax stresses faster than they build up.

Pavement Slippage. Slippage occurs when of tack coats and primes are not used properly.

Fatigue Failure. There are suggestions that asphalt could be modified to increase its stiffness so that the pavement thickness could be reduced. Again it must be remembered that it is the aggregate that carries the load, in compression, not the asphalt. However fatigue failure occurs in tension, and again the tensile strength of asphalt is much less than that of aggregate. The pavement is stretched underneath the wheel path, and between the wheel paths. However, tensile failure is often really crack propagation, thus additives that stop crack propagation such as tire buffings may be of value.,


Leave a Reply

Fill in your details below or click an icon to log in: Logo

You are commenting using your account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s